Mataas na Durability PETG Film
Mataas na Durability PETG Film is a thermoplastic polyester film based on polyethylene terephthalate glycol-modified resin. The glycol modification reduces the crystallization tendency of standard PET, producing an amorphous sheet with higher impact resistance and better thermoforming range. The film is supplied in thicknesses from 0.25 mm to 6.0 mm, in widths up to 2.1 m, with clear, colored, and frosted surface options. Impact strength reaches 8 to 12 kJ/m² by Charpy notched testing, and the film resists crazing under repeated flexural loading. High Durability PETG Film is specified for machine guards, signage, protective barriers, and thermoformed components where optical clarity and impact resistance are required together over a long service period.
Pasadyang Programa ng Pelikula
Mataas na Durability PETG Film is supplied under an ODM/OEM arrangement. Thickness, width, surface finish, color, and cut format are set according to the buyer's drawing or performance brief. Clear and tinted grades, matte and anti-glare surfaces, and hard-coated variants are developed and documented against a single approved specification sheet, and the approved sheet governs every production lot.
Profile ng Pagganap
Epekto sa Pagsipsip ng Enerhiya
Mataas na Durability PETG Film absorbs impact energy through ductile deformation rather than brittle fracture. Charpy notched impact values of 8 to 12 kJ/m² are maintained at temperatures from -20°C to 40°C, so the film retains its protective function in outdoor and cold-storage installations where acrylic sheet cracks.
Flexural Fatigue Resistance
Ang amorphous na istraktura ng pelikula ay pinahihintulutan ang paulit-ulit na baluktot nang walang pagpapaputi ng stress. Flexural fatigue testing sa ASTM D671 ay hindi nagbabalik ng crack initiation pagkatapos ng 100,000 cycle sa 0.5% strain amplitude, na sumusuporta sa paggamit sa mga hinged guard, display fixture, at flexible barrier panel.
Optical na kalinawan
Ang mga malinaw na grado ng High Durability PETG Film ay nagpapadala ng 84% hanggang 90% ng nakikitang liwanag na may haze value na mas mababa sa 1.0%. Ang ibabaw ay hindi dilaw sa ilalim ng panloob na pag-iilaw sa loob ng 10-taong panahon, at ang UV-stabilized na mga marka ay nagtataglay ng pagbabago ng kulay sa loob ng Delta E 2.0 sa ilalim ng 2,000 oras ng pinabilis na weathering.
Paglaban sa Kemikal at Paglilinis
Ang pelikula ay lumalaban sa diluted alkaline cleaners, neutral detergents, at alcohol-based sanitizers. Ang paglaban sa mga aromatic solvents at ketones ay limitado; ang mga ahente ng paglilinis batay sa mga kemikal na iyon ay nag-aalis ng kinang sa ibabaw at hindi kasama sa protocol ng pagpapanatili.
Saklaw ng Thermoforming
Mataas na Durability PETG Film forms at 120°C to 160°C with a wide processing window. Deep draws and complex shapes are produced without pre-drying, and the formed part retains impact resistance at the stretched corners. Mold shrinkage is 0.2% to 0.6%, consistent across production runs.
Dimensional Stability
Ang pelikula ay nagtataglay ng mga hiwa nitong dimensyon sa mga pagbabago sa halumigmig mula 20% hanggang 80% na kamag-anak na halumigmig. Ang linear thermal expansion ay 6.5 x 10⁻⁵ bawat °C, maihahambing sa aluminum, na nagpapasimple sa disenyo ng frame kung saan ang pelikula ay naka-mount sa pagitan ng mga metal extrusions.
Teknikal na Data
Mga Patlang ng Application
Mga Tanong ng Mamimili
Paano inihahambing ang PETG sa acrylic para sa mga epekto ng aplikasyon?
Mataas na Durability PETG Film provides higher impact resistance than cast acrylic at the same thickness, with Charpy notched values of 8 to 12 kJ/m² against typical acrylic values below 2 kJ/m². Acrylic offers higher surface hardness and better scratch resistance. For barrier and guard applications, PETG is specified; for high-scratch display faces, acrylic or a hard-coated PETG grade is preferred.
Kailangan ba ang pagpapatuyo bago ang thermoforming?
Mataas na Durability PETG Film does not require pre-drying in the normal shop environment. The film absorbs less than 0.2% moisture at 50% relative humidity, and that moisture level does not cause surface defects during forming. If the film has been stored in high humidity for an extended period, a 2-hour dry cycle at 65°C is recommended before forming thick-gauge sheet above 4.0 mm.
Anong mga cutting at edge finishing method ang angkop?
Ang pelikula ay pinutol ng CNC router, laser, saw, o die cutting. Ang pagputol ng laser ay nag-iiwan ng makintab na gilid ngunit maaaring makabuo ng bahagyang tint ng amber sa hiwa na linya; Ang pagruruta ng CNC na may matalas na single-flute bit ay gumagawa ng malinis na gilid. Ang pag-polish ng gilid gamit ang apoy o isang solvent na punasan ay nag-aalis ng mga marka ng router at nililinaw ang gilid para sa mga nakikitang aplikasyon.
Paano dapat linisin ang pelikula sa serbisyo?
Linisin gamit ang isang malambot na tela at isang neutral na solusyon sa detergent o isang alcohol-based na sanitizer. Banlawan ng malinis na tubig at tuyo gamit ang microfiber cloth. Huwag gumamit ng mga panlinis ng salamin na nakabatay sa ammonia, acetone, o mga nakasasakit na pad, na umaatake sa ibabaw at nagpapababa ng kalinawan. Para sa mga hard-coated na grado, sundin ang mga tagubilin sa pagpapanatili ng supplier ng coating.
Maaari bang maiugnay ang pelikula sa iba pang mga materyales?
Mataas na Durability PETG Film bonds to rigid substrates with solvent-free PU adhesive, acrylic adhesive tape, or structural acrylic adhesive. Solvent-based adhesives containing ketones or aromatic solvents attack the film surface and cause crazing. Test coupon bonding should be completed before production, particularly where the assembly will be exposed to temperature cycling.
Mga Tala sa Paghawak at Pag-iimbak
- Mag-imbak ng High Durability PETG Film sheet na patag sa isang matibay na papag sa isang tuyong lugar sa 10°C hanggang 30°C. Huwag sandalan ang mga sheet sa dingding nang matagal; ang sheet ay maaaring yumuko sa ilalim ng sarili nitong timbang.
- Panatilihin ang protective masking film sa lugar habang pinuputol at hinahawakan upang maiwasan ang mga gasgas sa ibabaw. Alisin ang masking sa loob ng 30 araw ng paghahatid upang maiwasan ang malagkit na paglipat sa ibabaw ng pelikula.
- Linisin ang pelikula gamit ang isang malambot na tela at neutral na detergent. Nakakasira sa ibabaw ang mga abrasive pad, ammonia-based na panlinis, at solvent-based na mga produkto na naglalaman ng mga ketone o aromatics.
- Suportahan ang buong lugar ng sheet sa panahon ng transportasyon at pag-install. Ang hindi suportadong mga gilid ng thin-gauge sheet ay maaaring lumihis at pumutok kapag itinaas sa isang punto.
- Para sa mga outdoor installation, tukuyin ang UV-stabilized grade at kumpirmahin na ang fixing system ay nagbibigay-daan sa thermal expansion na 6.5 x 10⁻⁵ bawat °C nang hindi pinipigilan ang gilid ng panel.